A novel method for characterizing temperature-dependent elastic modulus and glass transition temperature by processing the images of bending cantilever slender beams at different temperatures

Although measurements of crystallinity index (CI) have a long history, it has been found that CI varies significantly depending on the choice of measurement method. In this study, four different techniques incorporating X-ray diffraction and solid-state 13C nuclear magnetic resonance (NMR) were compared using eight different cellulose preparations. We found that the simplest method, which is also the most widely used, and which involves measurement of just two heights in the X-ray diffractogram, produced significantly higher crystallinity values than did the other methods. Data in the literature for the cellulose preparation used (Avicel PH-101) support this observation. We believe that the alternative X-ray diffraction (XRD) and NMR methods presented here, which consider the contributions from amorphous and crystalline cellulose to the entire XRD and NMR spectra, provide a more accurate measure of the crystallinity of cellulose. Although celluloses having a high amorphous content are usually more easily digested by enzymes, it is unclear, based on studies published in the literature, whether CI actually provides a clear indication of the digestibility of a cellulose sample. Cellulose accessibility should be affected by crystallinity, but is also likely to be affected by several other parameters, such as lignin/hemicellulose contents and distribution, porosity, and particle size. Given the methodological dependency of cellulose CI values and the complex nature of cellulase interactions with amorphous and crystalline celluloses, we caution against trying to correlate relatively small changes in CI with changes in cellulose digestibility. In addition, the prediction of cellulase performance based on low levels of cellulose conversion may not include sufficient digestion of the crystalline component to be meaningful.

The mechanical properties of bone tissue are determined by composition as well as structural, microstructural and nanostructural organization. The aim of this study was to quantify the elastic properties of bone at the lamellar level and compare these properties among osteonal, interstitial and trabecular microstructures from the diaphysis and the neck of the human femur. A nanoindentation technique with a custom irrigation system was used for simultaneously measuring force and displacement of a diamond tip pressed 500 nm into the moist bone tissue. An isotropic elastic modulus was calculated from the unloading curve with an assumed Poisson ratio of 0.3, while hardness was defined as the maximal force divided by the corresponding contact area. The elastic moduli ranged from 6.9 +/- 4.3 GPa in trabecular tissue from the femoral neck of a 74 yr old female up to 25.0 +/- 4.3 GPa in interstitial tissue from the diaphyseal cortex of a 69 yr old female. The mean elastic modulus was found to be significantly influenced by the type of lamella (p < 10(-6)) and by donor (p < 10(-6)). The interaction between the type of lamella and the donor was also highly significant (p < 10(-6)). Hardness followed a similar distribution as elastic modulus among types of lamellae and donor, but with lower statistical contrast. It is concluded that the nanostructure of bone tissue must differ substantially among lamellar types, anatomical sites and individuals and suggests that tissue heterogeneity is of potential importance in bone fragility and adaptation.