Materials for stretchable electronics

Electronics that are capable of intimate, non-invasive integration with the soft, curvilinear surfaces of biological tissues offer important opportunities for diagnosing and treating disease and for improving brain/machine interfaces. This article describes a material strategy for a type of bio-interfaced system that relies on ultrathin electronics supported by bioresorbable substrates of silk fibroin. Mounting such devices on tissue and then allowing the silk to dissolve and resorb initiates a spontaneous, conformal wrapping process driven by capillary forces at the biotic/abiotic interface. Specialized mesh designs and ultrathin forms for the electronics ensure minimal stresses on the tissue and highly conformal coverage, even for complex curvilinear surfaces, as confirmed by experimental and theoretical studies. In vivo, neural mapping experiments on feline animal models illustrate one mode of use for this class of technology. These concepts provide new capabilities for implantable and surgical devices. Show more

This paper describes the compatibility of poly(dimethylsiloxane) (PDMS) with organic solvents; this compatibility is important in considering the potential of PDMS-based microfluidic devices in a number of applications, including that of microreactors for organic reactions. We considered three aspects of compatibility: the swelling of PDMS in a solvent, the partitioning of solutes between a solvent and PDMS, and the dissolution of PDMS oligomers in a solvent. Of these three parameters that determine the compatibility of PDMS with a solvent, the swelling of PDMS had the greatest influence. Experimental measurements of swelling were correlated with the solubility parameter, delta (cal(1/2) cm(-3/2)), which is based on the cohesive energy densities, c (cal/cm(3)), of the materials. Solvents that swelled PDMS the least included water, nitromethane, dimethyl sulfoxide, ethylene glycol, perfluorotributylamine, perfluorodecalin, acetonitrile, and propylene carbonate; solvents that swelled PDMS the most were diisopropylamine, triethylamine, pentane, and xylenes. Highly swelling solvents were useful for extracting contaminants from bulk PDMS and for changing the surface properties of PDMS. The feasibility of performing organic reactions in PDMS was demonstrated by performing a Diels-Alder reaction in a microchannel. Show more

Recently there is strong interest in lightweight, flexible, and wearable electronics to meet the technological demands of modern society. Integrated energy storage devices of this type are a key area that is still significantly underdeveloped. Here, we describe wearable power devices using everyday textiles as the platform. With an extremely simple "dipping and drying" process using single-walled carbon nanotube (SWNT) ink, we produced highly conductive textiles with conductivity of 125 S cm(-1) and sheet resistance less than 1 Omega/sq. Such conductive textiles show outstanding flexibility and stretchability and demonstrate strong adhesion between the SWNTs and the textiles of interest. Supercapacitors made from these conductive textiles show high areal capacitance, up to 0.48F/cm(2), and high specific energy. We demonstrate the loading of pseudocapacitor materials into these conductive textiles that leads to a 24-fold increase of the areal capacitance of the device. These highly conductive textiles can provide new design opportunities for wearable electronics and energy storage applications. Show more