High valence state of Ni and Mo synergism in NiS2-MoS2 hetero-nanorods catalyst with layered surface structure for urea electrocatalysis

Objective comparisons of electrocatalyst activity and stability using standard methods under identical conditions are necessary to evaluate the viability of existing electrocatalysts for integration into solar-fuel devices as well as to help inform the development of new catalytic systems. Herein, we use a standard protocol as a primary screen for evaluating the activity, short-term (2 h) stability, and electrochemically active surface area (ECSA) of 18 electrocatalysts for the hydrogen evolution reaction (HER) and 26 electrocatalysts for the oxygen evolution reaction (OER) under conditions relevant to an integrated solar water-splitting device in aqueous acidic or alkaline solution. Our primary figure of merit is the overpotential necessary to achieve a magnitude current density of 10 mA cm(-2) per geometric area, the approximate current density expected for a 10% efficient solar-to-fuels conversion device under 1 sun illumination. The specific activity per ECSA of each material is also reported. Among HER catalysts, several could operate at 10 mA cm(-2) with overpotentials <0.1 V in acidic and/or alkaline solutions. Among OER catalysts in acidic solution, no non-noble metal based materials showed promising activity and stability, whereas in alkaline solution many OER catalysts performed with similar activity achieving 10 mA cm(-2) current densities at overpotentials of ~0.33-0.5 V. Most OER catalysts showed comparable or better specific activity per ECSA when compared to Ir and Ru catalysts in alkaline solutions, while most HER catalysts showed much lower specific activity than Pt in both acidic and alkaline solutions. For select catalysts, additional secondary screening measurements were conducted including Faradaic efficiency and extended stability measurements.

Two Ni–Mo–O compounds show exceptional cathodic/anodic catalytic performance for urea electrolysis, suggesting a promising route to energy-saving H 2 production. Photo/electrochemical splitting of water to hydrogen (H 2 ) fuel is a sustainable way of meeting our energy demands at no environmental cost, but significant challenges remain: for example, the sluggish anodic reaction imposes a considerable overpotential requirement. By contrast, urea electrolysis offers the prospect of energy-saving H 2 production together with urea-rich wastewater purification, whereas the lack of inexpensive and efficient urea oxidation reaction (UOR) catalysts places constraints on the development of this technique. Here we report a porous rod-like NiMoO 4 with high oxidation states of the metal elements enabling highly efficient UOR electrocatalysis, which can be readily produced through annealing solid NiMoO 4 · x H 2 O as a starting precursor in Ar. This precursor gives the derived Ni/NiO/MoO x nanocomposite when switching the shielding gas from Ar to H 2 /Ar, exhibiting platinum-like activity for the hydrogen evolution reaction (HER) in alkaline electrolytes. Assembling an electrolytic cell using our developed UOR and HER catalysts as the anode and cathode can provide a current density of 10 milliamperes per square centimeter at a cell voltage of mere 1.38 volts, as well as remarkable operational stability, representing the best yet reported noble-metal-free urea electrolyser. Our results demonstrate the potential of nickel–molybdenum-based materials as efficient electrode catalysts for urea electrolysers that promises cost-effective and energy-saving H 2 production.