ABSTRACT: Ready mix mortar is a ready to use mixture that uses hydration stabilizing (HSA) and air-entrained (AEA) admixtures in its composition, which modify its properties, especially the setting times. HSA extends the setting time of mortars for a long period, while AEA promotes a greater workability to the mixture. The study determined the temperature of the mortars with the evaluation of the setting times obtained by a semi-adiabatic calorimeter. Two types of cement (CPII-F-40 e CPII-Z-32) and varied contents of HSA (0.0%, 0.6% e 0.9%) and AEA (0.0%, 0.2% e 0.4%) were used. The results showed that the use of HSA decreased the amplitude of the temperature peaks and increased the setting times with cement CPII-Z-32 in relation to cement CPII-F-40. The setting time of the mortars was influenced by the type of cement used and by the contents of the admixtures.
RESUMO: A argamassa estabilizada é uma mistura pronta que faz uso dos aditivos estabilizador de hidratação (AEH) e incorporador de ar (AIA) em sua composição, os quais modificam suas propriedades, principalmente, os tempos de pega. O AEH prorroga o tempo de pega das argamassas por um longo período, enquanto o AIA promove maior trabalhabilidade à mistura. O estudo determinou a temperatura de argamassas com a avaliação dos tempos de pega obtidos em calorímetro semi-adiabático. Foram utilizados dois tipos de cimento (CPII-F-40 e CPII-Z-32) e variados os teores de AEH (0.0%, 0.6% e 0.9%) e AIA (0.0%, 0.2% e 0.4%). Os resultados mostraram que o uso de AEH diminuiu a amplitude dos picos de temperatura e aumentou os tempos de pega das argamassas com o cimento CPII-Z-32 em relação ao cimento CPII-F-40. O tempo de pega das argamassas foi influenciado pelo tipo do cimento utilizado e pelos teores de aditivos.